Product Details:
|
| Name: | PAI Plastic Hollow Tube | Place Of Origin: | Shenzhen, Guangdong |
|---|---|---|---|
| Burning Flame: | Dark Green | Color: | Customized |
| Packing: | Wooden Box | MOQ: | 1 Pcs |
| Free Sample: | Yes | Diameter: | 1-300mm |
| High Light: | 1-300mm PAI tubes,300mm PAI tubes plastic hollow,1-300mm PAI peek rod suppliers |
||
PAI plastic hollow tube High Performance Plastics
PAI board classification:
TORLON 4203 PAI (Amber)
It is the best in toughness and impact strength among PAI. Because of its inherent high temperature resistance, dimensional stability and good machinability. TORLON 4203 PAI is often used in the production of precision parts for high-tech equipment. Moreover, due to its good electrical insulation, it has been widely used in the field of electrical components.
TORLON 4301 PAI (black)
Filled with PTFE and graphite, compared with unfilled ones, it has better abrasion resistance and low friction coefficient. TORLON 4301PAI also shows excellent dimensional stability in a wide temperature range. This grade of material is mostly used in occasions with extremely high wear resistance requirements, such as non-lubricated bearings, seals, bearing isolation rings and reciprocating compressor parts.
TORLON 5530 PAI (black)
Filled with 30% glass fiber reinforced, compared with TORLON 4203 PAI, it exhibits good rigidity, high strength and good creep resistance. It is very suitable for manufacturing structural parts, supporting fixed load work for a long time under high temperature. And because TORLON 5530 PAI exhibits excellent dimensional stability at 250 ℃, it is very commonly used in the production of precision parts, such as the electronics and semiconductor industries. Regarding the use of TORLON 5530 PAI as a sliding part, its adaptability should be carefully checked because the glass fiber will scratch the surface.
|
Property |
Item No. |
Unit |
TORLON®4203PAI |
TORLON®4301PAI |
TORLON® 5530PAI |
| 1 |
Density |
g/cm3 |
1.41 | 1.45 | 1.61 |
| 2 |
Water absorption (223℃ in air) |
％ |
2.5 | 1.9 | 1.7 |
| 3 |
Tensile strength |
MPa |
120 | 80 | 95 |
| 4 |
Tensile strain at break |
％ |
10 | 5 | 3 |
| 5 |
Compressive stress(at 2%nominal strain) |
MPa |
53 | 58 | -- |
| 6 |
Charpy impact strength (unnotched) |
KJ/m2 |
No break |
-- | -- |
| 7 |
Charpy impact strength (notched) |
KJ/m2 |
10 | 4 | 3.5 |
| 8 |
Tensile modulus of elasticity |
MPa |
4500 | 5800 | 6000 |
| 9 |
Ball indentation hardness |
N/mm2 |
200 |
200 |
-- |
| 10 |
Rockwell hardness |
-- | E79 | M105 | E77 |