Product Details:
|
| Product Name: | Nylon Sheet | Length: | Customized (m) |
|---|---|---|---|
| Manufacturer: | Guangzhou City | Nylon Color: | Black White Blue Green Etc. |
| Nylon Board Brand: | Enqi | Nylon MOQ: | 1 Pc |
| Nylon Stability: | Against Organic Solvents And Fuels | Nylon Sample: | YES |
| Nylon Board Application: | High Hardness, Low Friction |
Beige wear-resistant oil-bearing mc nylon sheet PA66 General Engineering Plastics
The reason for the deformation of nylon parts is that it has high moisture absorption, and it can be placed in cold water to shape it immediately after being ejected from the mold. The post-treatment method is generally to use potassium acetate and boiling water to adjust the humidity to solve the deformation and internal stress, and then lathe processing, the ratio of potassium acetate to water is 1.25 to 1.
| Property | Item No. | Unit | MC Nylon (Natural) | Oil Nylon+Carbon (Black) | Oil Nylon (Green) | MC901 (Blue) | MC Nylon+MSO2 (Light black) |
| 1 | Density | g/cm3 | 1.15 | 1.15 | 1.135 | 1.15 | 1.16 |
| 2 | Water absorption (23℃ in air) | ％ | 1.8-2.0 | 1.8-2.0 | 2 | 2.3 | 2.4 |
| 3 | Tensile strength | MPa | 89 | 75.3 | 70 | 81 | 78 |
| 4 | Tensile strain at break | ％ | 29 | 22.7 | 25 | 35 | 25 |
| 5 | Compressive stress(at 2%nominal strain) | MPa | 51 | 51 | 43 | 47 | 49 |
| 6 | Charpy impact strength (unnotched) | KJ/m2 | No break | No break | ≥50 | No BK | No break |
| 7 | Charpy impact strength (notched) | KJ/m2 | ≥5.7 | ≥6.4 | 4 | 3.5 | 3.5 |
| 8 | Tensile modulus of elasticity | MPa | 3190 | 3130 | 3000 | 3200 | 3300 |
| 9 | Ball indentation hardness | N2 | 164 | 150 | 145 | 160 | 160 |
| 10 | Rockwell hardness | - | M88 | M87 | M82 | M85 | M84 |